GOST 5632 06Kh23N28 vs IS 1570 (Part 7) 12Cr12MoVH

Minimal Match — 32.7% match based on chemical composition and mechanical property overlap.

GOST 5632 06Kh23N28 (GOST 5632-2014) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. GOST 5632 06Kh23N28 is typically used for furnace components, heat exchangers, high temperature applications, while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, GOST 5632 06Kh23N28 vs IS 1570 (Part 7) 12Cr12MoVH is a 49.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32.7%.

Frequently Compared With GOST 5632 06Kh23N28:
EN 10088-1 1.4845 EN 10088-1 1.4301 EN 10088-1 1.4006 EN 10088-1 1.4401 ASTM A959 26-3-3 ASTM A959 16-8-2H ASTM A959 29-4 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH ASTM A959 201
Match Breakdown
CHEMISTRY MATCH
49.1%
MECHANICAL MATCH
0%
OVERALL
32.7%
Specifications
Property GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoVH
Standard GOST 5632-2014 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) ≤0.06 0.08-0.16
Si (%) ≤0.80 <=0.60
Mn (%) ≤2.00 0.40-1.00
Cr (%) 22.0–25.0 11.5-13.00
Ni (%) 26.0–29.0 <=1.0
P (%) Not specified <=0.040
S (%) Not specified <=0.035
Mo (%) Not specified 0.40-0.80
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength ≥510 MPa 770-930 MPa
Yield Strength ≥196 MPa >=585 MPa (0.2 % proof stress)
Elongation ≥35% >=15%
Max Service Temp 1050°C Not specified
Condition Not specified Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can GOST 5632 06Kh23N28 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
GOST 5632 06Kh23N28 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
IS 1570 (Part 7) 12Cr12MoVH
No active listings currently.
On M-EX Right Now
GOST 5632 06Kh23N28
2 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 5632 06Kh23N28 and IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 7) 12Cr12MoVH specifies P, S, Mo, V which are not specified for GOST 5632 06Kh23N28.
Can GOST 5632 06Kh23N28 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
GOST 5632 06Kh23N28 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.