Related Material — 56.9% match
based on chemical composition and mechanical property overlap.
GOST 5632 06Kh23N28 (GOST 5632-2014) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
GOST 5632 06Kh23N28 is typically used for furnace components, heat exchangers, high temperature applications, while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
EN 10088-1 1.4845 is defined under European Standard (EN) (Europe).
As per chemical composition, GOST 5632 06Kh23N28 vs EN 10088-1 1.4845 is a 85.4% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a related material overall at 56.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
GOST 5632 06Kh23N28
EN 10088-1 1.4845
Tensile Strength
≥510 MPa
≥515 MPa
Yield Strength
≥196 MPa
≥205 MPa
Elongation
≥35%
≥40%
Max Service Temp
1050°C
1100°C continuous
Typical Applications
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Can GOST 5632 06Kh23N28 Be Substituted With EN 10088-1 1.4845?
GOST 5632 06Kh23N28 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between GOST 5632 06Kh23N28 and EN 10088-1 1.4845?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can GOST 5632 06Kh23N28 be substituted with EN 10088-1 1.4845?
GOST 5632 06Kh23N28 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.