IS 11169 (Part 2) X02Cr17Ni12Mo2 vs EN 10088-1 X2CrNiMo17-12-2

Strong Match — 90.4% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr17Ni12Mo2 (IS 11169 (Part 2):1989) and EN 10088-1 X2CrNiMo17-12-2 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNiMo17-12-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X02Cr17Ni12Mo2 vs EN 10088-1 X2CrNiMo17-12-2 is a 90.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.4%.

Frequently Compared With IS 11169 (Part 2) X02Cr17Ni12Mo2:
ASTM A959 29-4C GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
90.4%
MECHANICAL MATCH
No shared data
OVERALL
90.4%
Specifications
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 EN 10088-1 X2CrNiMo17-12-2
Standard IS 11169 (Part 2):1989 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
Ni (%) 10.0-14.0 10.0-13.0
Cr (%) 16.0-18.0 16.5-18.5
Mo (%) 2.0-3.0 2.00-3.0
S (%) <=0.030 <=0.015
P (%) <=0.045 <=0.045
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 EN 10088-1 X2CrNiMo17-12-2
Yield Strength (0.2% proof) >=225 MPa Not specified
Tensile Strength 500-750 MPa Not specified
Elongation >=40% Not specified
Impact (U-notch 5 mm) >=60 J Not specified
Condition Quenched reference test piece (Table 6 treatment) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr17Ni12Mo2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
EN 10088-1 X2CrNiMo17-12-2
Not documented
Key Differences
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 Be Substituted With EN 10088-1 X2CrNiMo17-12-2?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and EN 10088-1 X2CrNiMo17-12-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMo17-12-2 is often considered as a substitute for IS 11169 (Part 2) X02Cr17Ni12Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr17Ni12Mo2
0 active listings and RFQs →
EN 10088-1 X2CrNiMo17-12-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr17Ni12Mo2 and EN 10088-1 X2CrNiMo17-12-2?
EN 10088-1 X2CrNiMo17-12-2 specifies N which is not specified for IS 11169 (Part 2) X02Cr17Ni12Mo2.
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 be substituted with EN 10088-1 X2CrNiMo17-12-2?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and EN 10088-1 X2CrNiMo17-12-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMo17-12-2 is often considered as a substitute for IS 11169 (Part 2) X02Cr17Ni12Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.