IS 11169 (Part 2) X02Cr19Ni10 vs BS 970 (Part 1) 304S11

Strong Match — 93.8% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr19Ni10 (IS 11169 (Part 2):1989) and BS 970 (Part 1) 304S11 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr19Ni10 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while BS 970 (Part 1) 304S11 is commonly used for austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (table 14, with table 15 for the cold drawn condition).. IS 11169 (Part 2) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 304S11 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 2) X02Cr19Ni10 vs BS 970 (Part 1) 304S11 is a 93.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.8%.

Frequently Compared With IS 11169 (Part 2) X02Cr19Ni10:
ASTM A959 201L GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
93.8%
MECHANICAL MATCH
No shared data
OVERALL
93.8%
Specifications
Property IS 11169 (Part 2) X02Cr19Ni10 BS 970 (Part 1) 304S11
Standard IS 11169 (Part 2):1989 BS 970 (Part 1):1983
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.0
Mn (%) <=2.0 <=2.0
Ni (%) 8.0-12.0 9.0-12.0
Cr (%) 17.5-20.0 17.0-19.0
S (%) <=0.030 <=0.030
P (%) <=0.045 <=0.045
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr19Ni10 BS 970 (Part 1) 304S11
Yield Strength (0.2% proof) >=175 MPa Not specified
Tensile Strength 450-700 MPa Not specified
Elongation >=50% Not specified
Impact (U-notch 5 mm) >=60 J Not specified
Condition Quenched reference test piece (Table 6 treatment) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr19Ni10
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
BS 970 (Part 1) 304S11
Austenitic stainless and heat resisting steel for mechanical and allied engineering purposes (Table 14, with Table 15 for the cold drawn condition).
Can IS 11169 (Part 2) X02Cr19Ni10 Be Substituted With BS 970 (Part 1) 304S11?
IS 11169 (Part 2) X02Cr19Ni10 and BS 970 (Part 1) 304S11 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 304S11 is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr19Ni10
0 active listings and RFQs →
BS 970 (Part 1) 304S11
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr19Ni10 and BS 970 (Part 1) 304S11?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X02Cr19Ni10 be substituted with BS 970 (Part 1) 304S11?
IS 11169 (Part 2) X02Cr19Ni10 and BS 970 (Part 1) 304S11 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 304S11 is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.