IS 11169 (Part 2) X02Cr19Ni10 vs EN 10088-1 X2CrNi18-9

Strong Match — 91% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr19Ni10 (IS 11169 (Part 2):1989) and EN 10088-1 X2CrNi18-9 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNi18-9 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X02Cr19Ni10 vs EN 10088-1 X2CrNi18-9 is a 91% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 91%.

Frequently Compared With IS 11169 (Part 2) X02Cr19Ni10:
ASTM A959 201L GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
91%
MECHANICAL MATCH
No shared data
OVERALL
91%
Specifications
Property IS 11169 (Part 2) X02Cr19Ni10 EN 10088-1 X2CrNi18-9
Standard IS 11169 (Part 2):1989 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
Ni (%) 8.0-12.0 8.0-10.5
Cr (%) 17.5-20.0 17.5-19.5
S (%) <=0.030 <=0.015
P (%) <=0.045 <=0.045
N (%) Not specified <=0.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr19Ni10 EN 10088-1 X2CrNi18-9
Yield Strength (0.2% proof) >=175 MPa Not specified
Tensile Strength 450-700 MPa Not specified
Elongation >=50% Not specified
Impact (U-notch 5 mm) >=60 J Not specified
Condition Quenched reference test piece (Table 6 treatment) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr19Ni10
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
EN 10088-1 X2CrNi18-9
Not documented
Key Differences
Can IS 11169 (Part 2) X02Cr19Ni10 Be Substituted With EN 10088-1 X2CrNi18-9?
IS 11169 (Part 2) X02Cr19Ni10 and EN 10088-1 X2CrNi18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNi18-9 is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr19Ni10
0 active listings and RFQs →
EN 10088-1 X2CrNi18-9
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr19Ni10 and EN 10088-1 X2CrNi18-9?
EN 10088-1 X2CrNi18-9 specifies N which is not specified for IS 11169 (Part 2) X02Cr19Ni10.
Can IS 11169 (Part 2) X02Cr19Ni10 be substituted with EN 10088-1 X2CrNi18-9?
IS 11169 (Part 2) X02Cr19Ni10 and EN 10088-1 X2CrNi18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNi18-9 is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.