IS 11169 (Part 2) X02Cr19Ni10 vs ASTM A959 304LN

Strong Match — 90.7% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr19Ni10 (IS 11169 (Part 2):1989) and ASTM A959 304LN (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr19Ni10 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while ASTM A959 304LN is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 304LN is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X02Cr19Ni10 vs ASTM A959 304LN is a 90.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.7%.

Frequently Compared With IS 11169 (Part 2) X02Cr19Ni10:
ASTM A959 201L GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10
Match Breakdown
CHEMISTRY MATCH
90.7%
MECHANICAL MATCH
No shared data
OVERALL
90.7%
Specifications
Property IS 11169 (Part 2) X02Cr19Ni10 ASTM A959 304LN
Standard IS 11169 (Part 2):1989 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
Ni (%) 8.0-12.0 8.0-11.0
Cr (%) 17.5-20.0 18.0-20.0
S (%) <=0.030 <=0.030
P (%) <=0.045 <=0.045
N (%) Not specified 0.10-0.16
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr19Ni10 ASTM A959 304LN
Yield Strength (0.2% proof) >=175 MPa Not specified
Tensile Strength 450-700 MPa Not specified
Elongation >=50% Not specified
Impact (U-notch 5 mm) >=60 J Not specified
Condition Quenched reference test piece (Table 6 treatment) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr19Ni10
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
ASTM A959 304LN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X02Cr19Ni10 Be Substituted With ASTM A959 304LN?
IS 11169 (Part 2) X02Cr19Ni10 and ASTM A959 304LN overlap closely enough on chemistry and mechanical properties that ASTM A959 304LN is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr19Ni10
0 active listings and RFQs →
ASTM A959 304LN
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr19Ni10 and ASTM A959 304LN?
ASTM A959 304LN specifies N which is not specified for IS 11169 (Part 2) X02Cr19Ni10.
Can IS 11169 (Part 2) X02Cr19Ni10 be substituted with ASTM A959 304LN?
IS 11169 (Part 2) X02Cr19Ni10 and ASTM A959 304LN overlap closely enough on chemistry and mechanical properties that ASTM A959 304LN is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.