IS 11169 (Part 2) X02Cr19Ni10 vs ASTM A959 201L

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr19Ni10 (IS 11169 (Part 2):1989) and ASTM A959 201L (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr19Ni10 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while ASTM A959 201L is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 201L is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X02Cr19Ni10 vs ASTM A959 201L is a 74.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 11169 (Part 2) X02Cr19Ni10:
GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
74.4%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 11169 (Part 2) X02Cr19Ni10 ASTM A959 201L
Standard IS 11169 (Part 2):1989 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.03
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 5.5-7.5
Ni (%) 8.0-12.0 3.5-5.5
Cr (%) 17.5-20.0 16.0-18.0
S (%) <=0.030 <=0.030
P (%) <=0.045 <=0.045
N (%) Not specified <=0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr19Ni10 ASTM A959 201L
Yield Strength (0.2% proof) >=175 MPa Not specified
Tensile Strength 450-700 MPa Not specified
Elongation >=50% Not specified
Impact (U-notch 5 mm) >=60 J Not specified
Condition Quenched reference test piece (Table 6 treatment) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr19Ni10
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
ASTM A959 201L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X02Cr19Ni10 Be Substituted With ASTM A959 201L?
IS 11169 (Part 2) X02Cr19Ni10 and ASTM A959 201L share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 2) X02Cr19Ni10
0 active listings and RFQs →
ASTM A959 201L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr19Ni10 and ASTM A959 201L?
ASTM A959 201L specifies N which is not specified for IS 11169 (Part 2) X02Cr19Ni10.
Can IS 11169 (Part 2) X02Cr19Ni10 be substituted with ASTM A959 201L?
IS 11169 (Part 2) X02Cr19Ni10 and ASTM A959 201L share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.