Minimal Match — 50.8% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X02Cr19Ni10 (IS 11169 (Part 2):1989) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X02Cr19Ni10 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
IS 11169 (Part 2) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 11169 (Part 2) X02Cr19Ni10 vs GOST 5632 08X18H10 is a 76.3% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 50.8%.
Frequently Compared With IS 11169 (Part 2) X02Cr19Ni10:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X02Cr19Ni10
GOST 5632 08X18H10
Yield Strength (0.2% proof)
>=175 MPa
Not specified
Tensile Strength
450-700 MPa
≥520 MPa
Elongation
>=50%
≥40%
Impact (U-notch 5 mm)
>=60 J
Not specified
Condition
Quenched reference test piece (Table 6 treatment)
Not specified
Yield Strength
Not specified
≥205 MPa
Typical Applications
IS 11169 (Part 2) X02Cr19Ni10
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Can IS 11169 (Part 2) X02Cr19Ni10 Be Substituted With GOST 5632 08X18H10?
IS 11169 (Part 2) X02Cr19Ni10 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X02Cr19Ni10 and GOST 5632 08X18H10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X02Cr19Ni10 be substituted with GOST 5632 08X18H10?
IS 11169 (Part 2) X02Cr19Ni10 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.