IS 11169 (Part 2) X02Cr19Ni10 vs EN 10088-1 1.4845
Minimal Match — 45.3% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X02Cr19Ni10 (IS 11169 (Part 2):1989) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X02Cr19Ni10 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
IS 11169 (Part 2) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 11169 (Part 2) X02Cr19Ni10 vs EN 10088-1 1.4845 is a 67.9% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 45.3%.
Frequently Compared With IS 11169 (Part 2) X02Cr19Ni10:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X02Cr19Ni10
EN 10088-1 1.4845
Yield Strength (0.2% proof)
>=175 MPa
Not specified
Tensile Strength
450-700 MPa
≥515 MPa
Elongation
>=50%
≥40%
Impact (U-notch 5 mm)
>=60 J
Not specified
Condition
Quenched reference test piece (Table 6 treatment)
Not specified
Yield Strength
Not specified
≥205 MPa
Max Service Temp
Not specified
1100°C continuous
Typical Applications
IS 11169 (Part 2) X02Cr19Ni10
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
IS 11169 (Part 2) X02Cr19Ni10 specifies S, P which are not specified for EN 10088-1 1.4845.
Can IS 11169 (Part 2) X02Cr19Ni10 Be Substituted With EN 10088-1 1.4845?
IS 11169 (Part 2) X02Cr19Ni10 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X02Cr19Ni10 and EN 10088-1 1.4845?
IS 11169 (Part 2) X02Cr19Ni10 specifies S, P which are not specified for EN 10088-1 1.4845.
Can IS 11169 (Part 2) X02Cr19Ni10 be substituted with EN 10088-1 1.4845?
IS 11169 (Part 2) X02Cr19Ni10 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.