IS 11169 (Part 2) X04Cr18Ni10Ti vs ASTM A959 347

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X04Cr18Ni10Ti (IS 11169 (Part 2):1989) and ASTM A959 347 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X04Cr18Ni10Ti is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while ASTM A959 347 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 347 is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X04Cr18Ni10Ti vs ASTM A959 347 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 11169 (Part 2) X04Cr18Ni10Ti:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property IS 11169 (Part 2) X04Cr18Ni10Ti ASTM A959 347
Standard IS 11169 (Part 2):1989 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
Ni (%) 9.0-12.0 9.0-12.0
Cr (%) 17.0-19.0 17.0-19.0
Ti (%) >=5xC, <=0.80 Not specified
S (%) <=0.030 <=0.030
P (%) <=0.045 <=0.045
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X04Cr18Ni10Ti ASTM A959 347
Yield Strength (0.2% proof) >=205 MPa Not specified
Tensile Strength 500-750 MPa Not specified
Elongation >=40% Not specified
Impact (U-notch 5 mm) >=60 J Not specified
Condition Quenched reference test piece (Table 6 treatment) Not specified
Typical Applications
IS 11169 (Part 2) X04Cr18Ni10Ti
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
ASTM A959 347
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X04Cr18Ni10Ti Be Substituted With ASTM A959 347?
IS 11169 (Part 2) X04Cr18Ni10Ti and ASTM A959 347 overlap closely enough on chemistry and mechanical properties that ASTM A959 347 is often considered as a substitute for IS 11169 (Part 2) X04Cr18Ni10Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X04Cr18Ni10Ti
0 active listings and RFQs →
ASTM A959 347
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X04Cr18Ni10Ti and ASTM A959 347?
IS 11169 (Part 2) X04Cr18Ni10Ti specifies Ti which is not specified for ASTM A959 347.
Can IS 11169 (Part 2) X04Cr18Ni10Ti be substituted with ASTM A959 347?
IS 11169 (Part 2) X04Cr18Ni10Ti and ASTM A959 347 overlap closely enough on chemistry and mechanical properties that ASTM A959 347 is often considered as a substitute for IS 11169 (Part 2) X04Cr18Ni10Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.