IS 11169 (Part 2) X04Cr18Ni10Ti vs EN 10088-1 1.4006
Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr18Ni10Ti (IS 11169 (Part 2):2023) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr18Ni10Ti is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments.
IS 11169 (Part 2) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 11169 (Part 2) X04Cr18Ni10Ti vs EN 10088-1 1.4006 is a 60.3% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 11169 (Part 2) X04Cr18Ni10Ti:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr18Ni10Ti
EN 10088-1 1.4006
Reduction of Area, solution annealed (+AT)
>=65% (over 5 to 50 mm)
Not specified
Tensile Strength, solution annealed (+AT)
<=680 MPa (over 5 to 50 mm)
Not specified
Tensile Strength
Not specified
≥540 MPa (annealed)
Hardness HRC
Not specified
36–45 (hardened)
Elongation
Not specified
≥18%
Typical Applications
IS 11169 (Part 2) X04Cr18Ni10Ti
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
IS 11169 (Part 2) X04Cr18Ni10Ti specifies Cu, P, S, Ti which are not specified for EN 10088-1 1.4006.
Can IS 11169 (Part 2) X04Cr18Ni10Ti Be Substituted With EN 10088-1 1.4006?
IS 11169 (Part 2) X04Cr18Ni10Ti and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Cr18Ni10Ti and EN 10088-1 1.4006?
IS 11169 (Part 2) X04Cr18Ni10Ti specifies Cu, P, S, Ti which are not specified for EN 10088-1 1.4006.
Can IS 11169 (Part 2) X04Cr18Ni10Ti be substituted with EN 10088-1 1.4006?
IS 11169 (Part 2) X04Cr18Ni10Ti and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.