IS 11169 (Part 2) X04Cr18Ni10Ti vs EN 10088-1 1.4845
Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr18Ni10Ti (IS 11169 (Part 2):2023) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr18Ni10Ti is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
IS 11169 (Part 2) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 11169 (Part 2) X04Cr18Ni10Ti vs EN 10088-1 1.4845 is a 65.5% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 11169 (Part 2) X04Cr18Ni10Ti:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr18Ni10Ti
EN 10088-1 1.4845
Reduction of Area, solution annealed (+AT)
>=65% (over 5 to 50 mm)
Not specified
Tensile Strength, solution annealed (+AT)
<=680 MPa (over 5 to 50 mm)
Not specified
Tensile Strength
Not specified
≥515 MPa
Yield Strength
Not specified
≥205 MPa
Elongation
Not specified
≥40%
Max Service Temp
Not specified
1100°C continuous
Typical Applications
IS 11169 (Part 2) X04Cr18Ni10Ti
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
IS 11169 (Part 2) X04Cr18Ni10Ti specifies Cu, P, S, Ti which are not specified for EN 10088-1 1.4845.
Can IS 11169 (Part 2) X04Cr18Ni10Ti Be Substituted With EN 10088-1 1.4845?
IS 11169 (Part 2) X04Cr18Ni10Ti and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Cr18Ni10Ti and EN 10088-1 1.4845?
IS 11169 (Part 2) X04Cr18Ni10Ti specifies Cu, P, S, Ti which are not specified for EN 10088-1 1.4845.
Can IS 11169 (Part 2) X04Cr18Ni10Ti be substituted with EN 10088-1 1.4845?
IS 11169 (Part 2) X04Cr18Ni10Ti and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.