IS 11169 (Part 2) X04Cr18Ni10Ti vs GB/T 3280 06Cr19Ni10
Related Material — 58.4% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr18Ni10Ti (IS 11169 (Part 2):2023) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr18Ni10Ti is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners..
IS 11169 (Part 2) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.
As per chemical composition, IS 11169 (Part 2) X04Cr18Ni10Ti vs GB/T 3280 06Cr19Ni10 is a 87.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a related material overall at 58.4%.
Frequently Compared With IS 11169 (Part 2) X04Cr18Ni10Ti:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr18Ni10Ti
GB/T 3280 06Cr19Ni10
Reduction of Area, solution annealed (+AT)
>=65% (over 5 to 50 mm)
Not specified
Tensile Strength, solution annealed (+AT)
<=680 MPa (over 5 to 50 mm)
Not specified
Tensile Strength
Not specified
520-720 MPa
Yield Strength
Not specified
205-310 MPa
Elongation
Not specified
40-60%
Hardness
Not specified
187 HB max
Typical Applications
IS 11169 (Part 2) X04Cr18Ni10Ti
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
IS 11169 (Part 2) X04Cr18Ni10Ti specifies Cu, Ti which are not specified for GB/T 3280 06Cr19Ni10.
Can IS 11169 (Part 2) X04Cr18Ni10Ti Be Substituted With GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X04Cr18Ni10Ti and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Cr18Ni10Ti and GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X04Cr18Ni10Ti specifies Cu, Ti which are not specified for GB/T 3280 06Cr19Ni10.
Can IS 11169 (Part 2) X04Cr18Ni10Ti be substituted with GB/T 3280 06Cr19Ni10?
IS 11169 (Part 2) X04Cr18Ni10Ti and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.