IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB vs EN 10088-1 1.4401
Minimal Match — 27.6% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB (IS 11169 (Part 2):2023) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while EN 10088-1 1.4401 is commonly used for marine, chemical processing, pharmaceutical equipment.
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB vs EN 10088-1 1.4401 is a 41.5% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 27.6%.
Frequently Compared With IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB
EN 10088-1 1.4401
Reduction of Area, cold drawn and solution annealed (+AT+C+AT)
>=65% (0.8 to 5 mm)
Not specified
Tensile Strength, cold drawn and solution annealed (+AT+C+AT)
<=780 MPa (0.8 to 2 mm) / <=730 MPa (over 2 to 5 mm)
Not specified
Tensile Strength
Not specified
≥520 MPa
Yield Strength
Not specified
≥210 MPa
Elongation
Not specified
≥40%
Hardness
Not specified
≤215 HB
Typical Applications
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB specifies Al, B, P, S which are not specified for EN 10088-1 1.4401.
Can IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB Be Substituted With EN 10088-1 1.4401?
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB and EN 10088-1 1.4401?
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB specifies Al, B, P, S which are not specified for EN 10088-1 1.4401.
Can IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB be substituted with EN 10088-1 1.4401?
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.