IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB vs GOST 5632 12Kh13
Minimal Match — 24.9% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB (IS 11169 (Part 2):2023) and GOST 5632 12Kh13 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while GOST 5632 12Kh13 is commonly used for turbine blades, pump shafts, fasteners, cutlery.
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB vs GOST 5632 12Kh13 is a 37.3% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 24.9%.
Frequently Compared With IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB
GOST 5632 12Kh13
Reduction of Area, cold drawn and solution annealed (+AT+C+AT)
>=65% (0.8 to 5 mm)
Not specified
Tensile Strength, cold drawn and solution annealed (+AT+C+AT)
<=780 MPa (0.8 to 2 mm) / <=730 MPa (over 2 to 5 mm)
Not specified
Tensile Strength
Not specified
≥540 MPa (annealed)
Hardness HRC
Not specified
36–45 (hardened)
Typical Applications
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
Key Differences
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB specifies Al, B, Mo, P which are not specified for GOST 5632 12Kh13.
Can IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB Be Substituted With GOST 5632 12Kh13?
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB and GOST 5632 12Kh13?
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB specifies Al, B, Mo, P which are not specified for GOST 5632 12Kh13.
Can IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB be substituted with GOST 5632 12Kh13?
IS 11169 (Part 2) X04Ni25Cr15Ti2Mo1VB and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.