IS 1570 (Part 4) 15Ni13Cr3Mo2 vs BS 970 (Part 1) 832M13

Strong Match — 90.4% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 15Ni13Cr3Mo2 (IS 1570 (Part 4):1988) and BS 970 (Part 1) 832M13 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 15Ni13Cr3Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 832M13 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 4) 15Ni13Cr3Mo2 vs BS 970 (Part 1) 832M13 is a 85.6% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 90.4%.

Frequently Compared With IS 1570 (Part 4) 15Ni13Cr3Mo2:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 IS 4367 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 10Mo6 IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
85.6%
MECHANICAL MATCH
100%
OVERALL
90.4%
Specifications
Property IS 1570 (Part 4) 15Ni13Cr3Mo2 BS 970 (Part 1) 832M13
Standard IS 1570 (Part 4):1988 BS 970 (Part 1):1991
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.10-0.16
Si (%) 0.15-0.35 Not specified
Mn (%) 0.30-0.60 0.35-0.60
Ni (%) 3.00-3.75 3.00-3.75
Cr (%) 0.60-1.10 0.70-1.00
Mo (%) 0.10-0.25 0.10-0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 15Ni13Cr3Mo2 BS 970 (Part 1) 832M13
Tensile Strength >=1080 MPa 1080 MPa min
Elongation >=8% 8 % min
Izod Impact >=35 J Not specified
Condition Case hardening steel, refined and quenched, core properties Case hardened, 19 mm test bar
Typical Applications
IS 1570 (Part 4) 15Ni13Cr3Mo2
Not documented
BS 970 (Part 1) 832M13
Case hardening steel (section four)
Key Differences
Can IS 1570 (Part 4) 15Ni13Cr3Mo2 Be Substituted With BS 970 (Part 1) 832M13?
IS 1570 (Part 4) 15Ni13Cr3Mo2 and BS 970 (Part 1) 832M13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 832M13 is often considered as a substitute for IS 1570 (Part 4) 15Ni13Cr3Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 4) 15Ni13Cr3Mo2
0 active listings and RFQs →
BS 970 (Part 1) 832M13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 15Ni13Cr3Mo2 and BS 970 (Part 1) 832M13?
IS 1570 (Part 4) 15Ni13Cr3Mo2 specifies Si which is not specified for BS 970 (Part 1) 832M13.
Can IS 1570 (Part 4) 15Ni13Cr3Mo2 be substituted with BS 970 (Part 1) 832M13?
IS 1570 (Part 4) 15Ni13Cr3Mo2 and BS 970 (Part 1) 832M13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 832M13 is often considered as a substitute for IS 1570 (Part 4) 15Ni13Cr3Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.