IS 1570 (Part 5) X02Cr17Ni12Mo2 vs ASTM A959 316L

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X02Cr17Ni12Mo2 (IS 1570 (Part 5):1985) and ASTM A959 316L (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X02Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 316L is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X02Cr17Ni12Mo2 vs ASTM A959 316L is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 1570 (Part 5) X02Cr17Ni12Mo2:
ASTM A959 29-4C ASTM A959 26-3-3 EN 10088-1 1.4401 GOST 5632 06Kh23N28 GOST 5632 12Kh13 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property IS 1570 (Part 5) X02Cr17Ni12Mo2 ASTM A959 316L
Standard IS 1570 (Part 5):1985 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.0-18.0 16.0-18.0
Ni (%) 10.0-14.0 10.0-14.0
Mo (%) 2.0-3.0 2.00-3.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X02Cr17Ni12Mo2 ASTM A959 316L
Tensile Strength >=485 MPa Not specified
Yield Strength >=170 MPa (0.2 % proof stress) Not specified
Elongation >=40% (50 mm) Not specified
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X02Cr17Ni12Mo2
Not documented
ASTM A959 316L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Can IS 1570 (Part 5) X02Cr17Ni12Mo2 Be Substituted With ASTM A959 316L?
IS 1570 (Part 5) X02Cr17Ni12Mo2 and ASTM A959 316L overlap closely enough on chemistry and mechanical properties that ASTM A959 316L is often considered as a substitute for IS 1570 (Part 5) X02Cr17Ni12Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X02Cr17Ni12Mo2
0 active listings and RFQs →
ASTM A959 316L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X02Cr17Ni12Mo2 and ASTM A959 316L?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X02Cr17Ni12Mo2 be substituted with ASTM A959 316L?
IS 1570 (Part 5) X02Cr17Ni12Mo2 and ASTM A959 316L overlap closely enough on chemistry and mechanical properties that ASTM A959 316L is often considered as a substitute for IS 1570 (Part 5) X02Cr17Ni12Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.