IS 1570 (Part 5) X02Cr19Ni10 vs EN 10088-1 1.4401

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X02Cr19Ni10 (IS 1570 (Part 5):1985) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X02Cr19Ni10 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X02Cr19Ni10 vs EN 10088-1 1.4401 is a 64.2% match. As per mechanical properties, the match is 25%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X02Cr19Ni10:
EN 10088-1 1.4845 ASTM A959 201L EN 10088-1 1.4006 EN 10088-1 1.4301 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
64.2%
MECHANICAL MATCH
25%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X02Cr19Ni10 EN 10088-1 1.4401
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.07
Si (%) <=1.0 ≤1.00
Mn (%) <=2.0 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 17.5-20.0 16.5–18.5
Ni (%) 8.0-12.0 10.5–13.5
Mo (%) Not specified 2.0–2.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X02Cr19Ni10 EN 10088-1 1.4401
Tensile Strength >=485 MPa ≥520 MPa
Yield Strength >=170 MPa (0.2 % proof stress) ≥210 MPa
Elongation >=40% (50 mm) ≥40%
Hardness <=183 HB; <=88 HRB ≤215 HB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X02Cr19Ni10
Not documented
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
Can IS 1570 (Part 5) X02Cr19Ni10 Be Substituted With EN 10088-1 1.4401?
IS 1570 (Part 5) X02Cr19Ni10 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X02Cr19Ni10
No active listings currently.
EN 10088-1 1.4401
Sheet → (4 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3400 mm (98.43–133.86 in)
On M-EX Right Now
IS 1570 (Part 5) X02Cr19Ni10
0 active listings and RFQs →
EN 10088-1 1.4401
4 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X02Cr19Ni10 and EN 10088-1 1.4401?
IS 1570 (Part 5) X02Cr19Ni10 specifies P, S which are not specified for EN 10088-1 1.4401. EN 10088-1 1.4401 specifies Mo which is not specified for IS 1570 (Part 5) X02Cr19Ni10.
Can IS 1570 (Part 5) X02Cr19Ni10 be substituted with EN 10088-1 1.4401?
IS 1570 (Part 5) X02Cr19Ni10 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.