IS 1570 (Part 5) X04Cr25Ni20 vs ASTM A276/A276M S31000

Strong Match — 96.2% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr25Ni20 (IS 1570 (Part 5):1985) and ASTM A276/A276M S31000 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr25Ni20 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A276/A276M S31000 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X04Cr25Ni20 vs ASTM A276/A276M S31000 is a 94.3% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 96.2%.

Frequently Compared With IS 1570 (Part 5) X04Cr25Ni20:
GOST 5632 06Kh23N28 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
94.3%
MECHANICAL MATCH
100%
OVERALL
96.2%
Specifications
Property IS 1570 (Part 5) X04Cr25Ni20 ASTM A276/A276M S31000
Standard IS 1570 (Part 5):1985 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.25
Si (%) <=1.5 <=1.50
Mn (%) <=2.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 24.0-26.0 24.0-26.0
Ni (%) 19.0-22.0 19.0-22.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr25Ni20 ASTM A276/A276M S31000
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa (0.2 % proof stress) >=205 MPa
Elongation >=40% (50 mm) >=40%
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Condition A (Annealed), hot-finished, all sizes (first row printed)
Typical Applications
IS 1570 (Part 5) X04Cr25Ni20
Not documented
ASTM A276/A276M S31000
Stainless steel bars and shapes (hot-finished or cold-finished)
Can IS 1570 (Part 5) X04Cr25Ni20 Be Substituted With ASTM A276/A276M S31000?
IS 1570 (Part 5) X04Cr25Ni20 and ASTM A276/A276M S31000 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S31000 is often considered as a substitute for IS 1570 (Part 5) X04Cr25Ni20 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X04Cr25Ni20
0 active listings and RFQs →
ASTM A276/A276M S31000
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr25Ni20 and ASTM A276/A276M S31000?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X04Cr25Ni20 be substituted with ASTM A276/A276M S31000?
IS 1570 (Part 5) X04Cr25Ni20 and ASTM A276/A276M S31000 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S31000 is often considered as a substitute for IS 1570 (Part 5) X04Cr25Ni20 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.