IS 1570 (Part 5) X15Cr25N vs ASTM A959 S41603

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X15Cr25N (IS 1570 (Part 5):1985) and ASTM A959 S41603 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X15Cr25N is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 S41603 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X15Cr25N vs ASTM A959 S41603 is a 77.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 5) X15Cr25N:
GOST 5632 06Kh23N28 GOST 5632 12Kh13 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
77.8%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 5) X15Cr25N ASTM A959 S41603
Standard IS 1570 (Part 5):1985 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.20 <=0.08
Si (%) <=1.0 <=1.00
Mn (%) <=1.5 <=1.25
P (%) <=0.045 <=0.06
S (%) <=0.030 >=0.15
Cr (%) 23.0-27.0 12.0-14.0
N (%) <=0.25 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X15Cr25N ASTM A959 S41603
Tensile Strength >=515 MPa Not specified
Yield Strength >=275 MPa (0.2 % proof stress) Not specified
Elongation >=20% (50 mm) Not specified
Hardness <=217 HB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X15Cr25N
Not documented
ASTM A959 S41603
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 1570 (Part 5) X15Cr25N Be Substituted With ASTM A959 S41603?
IS 1570 (Part 5) X15Cr25N and ASTM A959 S41603 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 5) X15Cr25N
0 active listings and RFQs →
ASTM A959 S41603
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X15Cr25N and ASTM A959 S41603?
IS 1570 (Part 5) X15Cr25N specifies N which is not specified for ASTM A959 S41603.
Can IS 1570 (Part 5) X15Cr25N be substituted with ASTM A959 S41603?
IS 1570 (Part 5) X15Cr25N and ASTM A959 S41603 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.