IS 1570 (Part 5) X85Cr18Mo2V vs IS 11169 (Part 2) X04Cr17Mo1

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X85Cr18Mo2V (IS 1570 (Part 5):1985) and IS 11169 (Part 2) X04Cr17Mo1 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X85Cr18Mo2V is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 2) X04Cr17Mo1 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 5) X85Cr18Mo2V vs IS 11169 (Part 2) X04Cr17Mo1 is a 74.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 5) X85Cr18Mo2V:
GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr12MoH GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
74.5%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 5) X85Cr18Mo2V IS 11169 (Part 2) X04Cr17Mo1
Standard IS 1570 (Part 5):1985 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) 0.80-0.90 <=0.08
Si (%) <=1.0 <=1.00
Mn (%) <=1.5 <=1.00
P (%) <=0.045 <=0.040
S (%) <=0.035 <=0.030
Cr (%) 16.5-18.5 16.0-18.0
Mo (%) <=2.5 0.75-1.40
V (%) <=0.60 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X85Cr18Mo2V IS 11169 (Part 2) X04Cr17Mo1
Hardness 255-306 HB Not specified
Condition Valve steel, hardened and tempered (Table 6) Not specified
Reduction of Area, soft annealed (+A) Not specified >=60% (over 5 to 25 mm)
Tensile Strength, soft annealed (+A) Not specified <=600 MPa (over 5 to 25 mm)
Typical Applications
IS 1570 (Part 5) X85Cr18Mo2V
Not documented
IS 11169 (Part 2) X04Cr17Mo1
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
Key Differences
Can IS 1570 (Part 5) X85Cr18Mo2V Be Substituted With IS 11169 (Part 2) X04Cr17Mo1?
IS 1570 (Part 5) X85Cr18Mo2V and IS 11169 (Part 2) X04Cr17Mo1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 5) X85Cr18Mo2V
0 active listings and RFQs →
IS 11169 (Part 2) X04Cr17Mo1
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X85Cr18Mo2V and IS 11169 (Part 2) X04Cr17Mo1?
IS 1570 (Part 5) X85Cr18Mo2V specifies V which is not specified for IS 11169 (Part 2) X04Cr17Mo1.
Can IS 1570 (Part 5) X85Cr18Mo2V be substituted with IS 11169 (Part 2) X04Cr17Mo1?
IS 1570 (Part 5) X85Cr18Mo2V and IS 11169 (Part 2) X04Cr17Mo1 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.