IS 1570 (Part 7) Fe410H vs IS 1570 (Part 7) Fe360H

Close Alternative — 70.7% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) Fe410H (IS 1570 (Part 7):1992) and IS 1570 (Part 7) Fe360H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 7) Fe410H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while IS 1570 (Part 7) Fe360H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 1570 (Part 7) Fe410H is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) Fe360H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 7) Fe410H vs IS 1570 (Part 7) Fe360H is a 98.7% match. As per mechanical properties, the match is 14.6%. Combined, this makes them a close alternative overall at 70.7%.

Frequently Compared With IS 1570 (Part 7) Fe410H:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
98.7%
MECHANICAL MATCH
14.6%
OVERALL
70.7%
Specifications
Property IS 1570 (Part 7) Fe410H IS 1570 (Part 7) Fe360H
Standard IS 1570 (Part 7):1992 IS 1570 (Part 7):1992
Category Carbon Steel Carbon Steel
C (%) <=0.20 <=0.20
Si (%) 0.10-0.35 0.10-0.35
Mn (%) 0.50-1.30 0.40-1.20
P (%) <=0.03 <=0.03
S (%) <=0.03 <=0.03
Cr (%) <=0.25 <=0.25
Ni (%) <=0.30 <=0.30
Mo (%) <=0.10 <=0.10
Cu (%) <=0.30 <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) Fe410H IS 1570 (Part 7) Fe360H
Tensile Strength 410-520 MPa 360-480 MPa
Yield Strength >=225 MPa (0.2 % proof stress) >=205 MPa (0.2 % proof stress)
Elongation >=24% >=26%
Condition Plate, quadrangular seamless pipe, N, thickness over 3 to 16 (first row of Table 3) Plate, N, thickness over 3 to 16 (first row of Table 3)
Typical Applications
IS 1570 (Part 7) Fe410H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
IS 1570 (Part 7) Fe360H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Can IS 1570 (Part 7) Fe410H Be Substituted With IS 1570 (Part 7) Fe360H?
IS 1570 (Part 7) Fe410H and IS 1570 (Part 7) Fe360H are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 7) Fe410H
0 active listings and RFQs →
IS 1570 (Part 7) Fe360H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) Fe410H and IS 1570 (Part 7) Fe360H?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 7) Fe410H be substituted with IS 1570 (Part 7) Fe360H?
IS 1570 (Part 7) Fe410H and IS 1570 (Part 7) Fe360H are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.