IS 2062 E410A vs IS 2062 E250B0

Close Alternative — 76.6% match based on chemical composition and mechanical property overlap.

IS 2062 E410A (IS 2062:2011) and IS 2062 E250B0 (IS 2062:2011) are both steel grades. Both fall under the Structural Steel category. IS 2062 E410A is typically used for high strength structural applications, while IS 2062 E250B0 is commonly used for structural sections, welded structures, bridges, transmission towers, industrial fabrication, engineering structures. IS 2062 E410A is defined under Bureau of Indian Standards (IS), originating from India, while IS 2062 E250B0 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 2062 E410A vs IS 2062 E250B0 is a 98.2% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a close alternative overall at 76.6%.

Frequently Compared With IS 2062 E410A:
AS/NZS 3679.1 350 CSA G40.21 400W CSA G40.21 350W CSA G40.21 260W CSA G40.21 300W CSA G40.21 400A GOST 19281 09G2S AS/NZS 3679.1 300 CSA G40.21 480W IS 2062 E250A ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80
Match Breakdown
CHEMISTRY MATCH
98.2%
MECHANICAL MATCH
33.3%
OVERALL
76.6%
Specifications
Property IS 2062 E410A IS 2062 E250B0
Standard IS 2062:2011 IS 2062:2011
Category Structural Steel Structural Steel
C (%) <=0.20 <=0.22
Mn (%) <=1.60 <=1.50
Si (%) <=0.45 <=0.40
S (%) <=0.045 <=0.045
P (%) <=0.045 <=0.045
CEV (%) <=0.50 <=0.41
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 E410A IS 2062 E250B0
Tensile Strength >=540 MPa >=410 MPa
Yield Strength 410 MPa (<=20mm) / 390 MPa (20-40mm) / 380 MPa (>40mm) 250 MPa (<=20mm) / 240 MPa (20-40mm) / 230 MPa (>40mm)
Elongation >=20% >=23%
Impact not required Not specified
Impact Energy Not specified >=27 J at 0°C
Typical Applications
IS 2062 E410A
High strength structural applications
IS 2062 E250B0
structural sections, welded structures, bridges, transmission towers, industrial fabrication, engineering structures
Can IS 2062 E410A Be Substituted With IS 2062 E250B0?
IS 2062 E410A and IS 2062 E250B0 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
IS 2062 E410A
Plate → (8 listings)
Thickness: 8–10 mm (0.31–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–4100 mm (98.43–161.42 in)
Angle → (6 listings)
Leg 1: 50–130 mm (1.97–5.12 in)
Leg 2: 130–6000 mm (5.12–236.22 in)
Thickness: 6–8 mm (0.24–0.31 in)
IS 2062 E250B0
Angle → (6 listings)
Leg 1: 25–30 mm (0.98–1.18 in)
Leg 2: 20–25 mm (0.79–0.98 in)
Thickness: 3–5 mm (0.12–0.2 in)
On M-EX Right Now
IS 2062 E410A
14 active listings and RFQs →
IS 2062 E250B0
6 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 E410A and IS 2062 E250B0?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 2062 E410A be substituted with IS 2062 E250B0?
IS 2062 E410A and IS 2062 E250B0 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.