IS 4367 07Cr4Mo6 vs IS 11169 (Part 1) 12Cr4Mo2

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 4367 07Cr4Mo6 (IS 4367:1991) and IS 11169 (Part 1) 12Cr4Mo2 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 12Cr4Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4367 07Cr4Mo6 vs IS 11169 (Part 1) 12Cr4Mo2 is a 58.9% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 4367 07Cr4Mo6:
IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 12Cr2Mo5V2H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 7) 12Cr4Mo5H UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 103Cr4
Match Breakdown
CHEMISTRY MATCH
58.9%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 4367 07Cr4Mo6 IS 11169 (Part 1) 12Cr4Mo2
Standard IS 4367:1991 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) <=0.12 0.10-0.15
Si (%) 0.15-0.60 <=0.30
Mn (%) 0.40-0.70 0.60-0.90
Ni (%) <=0.30 Not specified
Cr (%) 0.70-1.10 0.90-1.20
Mo (%) 0.45-0.65 0.15-0.25
S (%) <=0.035 <=0.025
P (%) <=0.035 <=0.025
Cu (%) Not specified <=0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 07Cr4Mo6 IS 11169 (Part 1) 12Cr4Mo2
Tensile Strength 380-550 MPa Not specified
Yield Strength 225 MPa min Not specified
Elongation >=19% Not specified
Izod Impact 60 J min Not specified
Hardness (soft annealed) <=170 HB Not specified
Condition Normalised and tempered, ruling section up to 40 mm Not specified
Hardness, ferrite-pearlite (+FP) Not specified 135-185 HB
Tensile Strength, annealed (+AC) Not specified <=500 MPa (over 5 to 40 mm)
Typical Applications
IS 4367 07Cr4Mo6
Not documented
IS 11169 (Part 1) 12Cr4Mo2
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can IS 4367 07Cr4Mo6 Be Substituted With IS 11169 (Part 1) 12Cr4Mo2?
IS 4367 07Cr4Mo6 and IS 11169 (Part 1) 12Cr4Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 4367 07Cr4Mo6
0 active listings and RFQs →
IS 11169 (Part 1) 12Cr4Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 07Cr4Mo6 and IS 11169 (Part 1) 12Cr4Mo2?
IS 4367 07Cr4Mo6 specifies Ni which is not specified for IS 11169 (Part 1) 12Cr4Mo2. IS 11169 (Part 1) 12Cr4Mo2 specifies Cu which is not specified for IS 4367 07Cr4Mo6.
Can IS 4367 07Cr4Mo6 be substituted with IS 11169 (Part 1) 12Cr4Mo2?
IS 4367 07Cr4Mo6 and IS 11169 (Part 1) 12Cr4Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.