Related Material — 58.1% match
based on chemical composition and mechanical property overlap.
IS 4367 07Cr4Mo6 (IS 4367:1991) and IS 4367 10Cr9Mo10 (IS 4367:1991) are both steel grades.
Both fall under the Alloy Steel category.
IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 10Cr9Mo10 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 4367 07Cr4Mo6 vs IS 4367 10Cr9Mo10 is a 78.8% match.
As per mechanical properties, the match is 16.7%.
Combined, this makes them a related material overall at 58.1%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 4367 07Cr4Mo6
IS 4367 10Cr9Mo10
Tensile Strength
380-550 MPa
410-590 MPa
Yield Strength
225 MPa min
245 MPa min
Elongation
>=19%
>=18%
Izod Impact
60 J min
55 J min
Hardness (soft annealed)
<=170 HB
<=187 HB
Condition
Normalised and tempered, ruling section up to 40 mm
Normalised and tempered, ruling section up to 50 mm
Can IS 4367 07Cr4Mo6 Be Substituted With IS 4367 10Cr9Mo10?
IS 4367 07Cr4Mo6 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 4367 07Cr4Mo6 and IS 4367 10Cr9Mo10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 4367 07Cr4Mo6 be substituted with IS 4367 10Cr9Mo10?
IS 4367 07Cr4Mo6 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.