IS 4367 07Cr4Mo6 vs IS 1570 (Part 4) 07Cr4Mo6

Strong Match — 98.3% match based on chemical composition and mechanical property overlap.

IS 4367 07Cr4Mo6 (IS 4367:1991) and IS 1570 (Part 4) 07Cr4Mo6 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 4) 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4367 07Cr4Mo6 vs IS 1570 (Part 4) 07Cr4Mo6 is a 98.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.3%.

Frequently Compared With IS 4367 07Cr4Mo6:
NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 12Cr2Mo5V2H IS 11169 (Part 1) 10Ni5Cr4 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 7) 12Cr4Mo5H IS 1570 (Part 4) 103Cr4 IS 11169 (Part 1) 12Cr4Mo2
Match Breakdown
CHEMISTRY MATCH
98.3%
MECHANICAL MATCH
No shared data
OVERALL
98.3%
Specifications
Property IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6
Standard IS 4367:1991 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) <=0.12 <=0.12
Si (%) 0.15-0.60 0.15-0.60
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) <=0.30 <=0.30
Cr (%) 0.70-1.10 0.70-1.10
Mo (%) 0.45-0.65 0.45-0.65
S (%) <=0.035 Not specified
P (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6
Tensile Strength 380-550 MPa Not specified
Yield Strength 225 MPa min Not specified
Elongation >=19% Not specified
Izod Impact 60 J min Not specified
Hardness (soft annealed) <=170 HB Not specified
Condition Normalised and tempered, ruling section up to 40 mm Not specified
Key Differences
Can IS 4367 07Cr4Mo6 Be Substituted With IS 1570 (Part 4) 07Cr4Mo6?
IS 4367 07Cr4Mo6 and IS 1570 (Part 4) 07Cr4Mo6 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 4) 07Cr4Mo6 is often considered as a substitute for IS 4367 07Cr4Mo6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 4367 07Cr4Mo6
0 active listings and RFQs →
IS 1570 (Part 4) 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 07Cr4Mo6 and IS 1570 (Part 4) 07Cr4Mo6?
IS 4367 07Cr4Mo6 specifies S, P which are not specified for IS 1570 (Part 4) 07Cr4Mo6.
Can IS 4367 07Cr4Mo6 be substituted with IS 1570 (Part 4) 07Cr4Mo6?
IS 4367 07Cr4Mo6 and IS 1570 (Part 4) 07Cr4Mo6 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 4) 07Cr4Mo6 is often considered as a substitute for IS 4367 07Cr4Mo6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.