IS 4432 C10 vs IS 1570 (Part 2/Sec 1) 10C4

Strong Match — 95.8% match based on chemical composition and mechanical property overlap.

IS 4432 C10 (IS 4432:1967) and IS 1570 (Part 2/Sec 1) 10C4 (IS 1570 (Part 2/Sec 1):1979) are both steel grades. Both fall under the Carbon Steel category. IS 4432 C10 is typically used for bolts, nuts, shafts, pins, general engineering parts, structural components, welded assemblies, while IS 1570 (Part 2/Sec 1) 10C4 is commonly used for wire for wood screws, welding electrode core wire and case hardened parts (the standard links this grade to is 1812, is 2879, is 4432). IS 4432 C10 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 2/Sec 1) 10C4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4432 C10 vs IS 1570 (Part 2/Sec 1) 10C4 is a 93.7% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 95.8%.

Frequently Compared With IS 4432 C10:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 045A10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
93.7%
MECHANICAL MATCH
100%
OVERALL
95.8%
Specifications
Property IS 4432 C10 IS 1570 (Part 2/Sec 1) 10C4
Standard IS 4432:1967 IS 1570 (Part 2/Sec 1):1979
Category Carbon Steel Carbon Steel
C (%) <=0.15 <=0.15
Mn (%) 0.30-0.60 0.30-0.60
Si (%) 0.15-0.35 Not specified
S (%) <=0.045 Not specified
P (%) <=0.045 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4432 C10 IS 1570 (Part 2/Sec 1) 10C4
Tensile Strength 340-420 MPa 340-420 MPa
Yield Strength >=187 MPa Not specified
Elongation >=26% >=26%
Hardness <=120 HB Not specified
Typical Applications
IS 4432 C10
bolts, nuts, shafts, pins, general engineering parts, structural components, welded assemblies
IS 1570 (Part 2/Sec 1) 10C4
Wire for wood screws, welding electrode core wire and case hardened parts (the standard links this grade to IS 1812, IS 2879, IS 4432)
Key Differences
Can IS 4432 C10 Be Substituted With IS 1570 (Part 2/Sec 1) 10C4?
IS 4432 C10 and IS 1570 (Part 2/Sec 1) 10C4 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 2/Sec 1) 10C4 is often considered as a substitute for IS 4432 C10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 4432 C10
Round Bar → (5 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5000–6900 mm (196.85–271.65 in)
IS 1570 (Part 2/Sec 1) 10C4
No active listings currently.
On M-EX Right Now
IS 4432 C10
5 active listings and RFQs →
IS 1570 (Part 2/Sec 1) 10C4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4432 C10 and IS 1570 (Part 2/Sec 1) 10C4?
IS 4432 C10 specifies Si, S, P which are not specified for IS 1570 (Part 2/Sec 1) 10C4.
Can IS 4432 C10 be substituted with IS 1570 (Part 2/Sec 1) 10C4?
IS 4432 C10 and IS 1570 (Part 2/Sec 1) 10C4 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 2/Sec 1) 10C4 is often considered as a substitute for IS 4432 C10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.