JIS G4303 SUS316 vs EN 10088-1 1.4301

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

JIS G4303 SUS316 (JIS G4303:2021) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. JIS G4303 SUS316 is typically used for marine applications, chemical processing, pharmaceutical equipment, while EN 10088-1 1.4301 is commonly used for food equipment, chemical vessels, architectural, kitchenware. JIS G4303 SUS316 is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4303 SUS316 vs EN 10088-1 1.4301 is a 76.9% match. As per mechanical properties, the match is 25%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With JIS G4303 SUS316:
EN 10088-1 1.4401 GOST 5632 08X18H10 GOST 5632 12Kh13 EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4845 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
76.9%
MECHANICAL MATCH
25%
OVERALL
35%
Specifications
Property JIS G4303 SUS316 EN 10088-1 1.4301
Standard JIS G4303:2021 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) ≤0.08 ≤0.07
Si (%) ≤1.00 ≤1.00
Mn (%) ≤2.00 ≤2.00
Cr (%) 16.0–18.0 17.5–19.5
Ni (%) 10.0–14.0 8.0–10.5
Mo (%) 2.0–3.0 Not specified
P (%) Not specified ≤0.045
S (%) Not specified ≤0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4303 SUS316 EN 10088-1 1.4301
Tensile Strength ≥520 MPa ≥520 MPa
Yield Strength ≥205 MPa ≥210 MPa
Elongation ≥40% ≥45%
Hardness ≤187 HB ≤215 HB
Typical Applications
JIS G4303 SUS316
Marine applications, chemical processing, pharmaceutical equipment
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
Can JIS G4303 SUS316 Be Substituted With EN 10088-1 1.4301?
JIS G4303 SUS316 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4303 SUS316
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2800–3300 mm (110.24–129.92 in)
EN 10088-1 1.4301
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3300 mm (98.43–129.92 in)
On M-EX Right Now
JIS G4303 SUS316
3 active listings and RFQs →
EN 10088-1 1.4301
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4303 SUS316 and EN 10088-1 1.4301?
JIS G4303 SUS316 specifies Mo which is not specified for EN 10088-1 1.4301. EN 10088-1 1.4301 specifies P, S which are not specified for JIS G4303 SUS316.
Can JIS G4303 SUS316 be substituted with EN 10088-1 1.4301?
JIS G4303 SUS316 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.