JIS G4303 SUS316 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

JIS G4303 SUS316 (JIS G4303:2021) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. JIS G4303 SUS316 is typically used for marine applications, chemical processing, pharmaceutical equipment, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. JIS G4303 SUS316 is defined under Japanese Industrial Standards (JIS) (Japan).

As per chemical composition, JIS G4303 SUS316 vs GOST 5632 08X18H10 is a 79.4% match. As per mechanical properties, the match is 100%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With JIS G4303 SUS316:
EN 10088-1 1.4401 GOST 5632 12Kh13 EN 10088-1 1.4006 GOST 5632 06Kh23N28 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
79.4%
MECHANICAL MATCH
100%
OVERALL
35%
Specifications
Property JIS G4303 SUS316 GOST 5632 08X18H10
Standard JIS G4303:2021 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) ≤0.08 ≤0.08
Si (%) ≤1.00 ≤0.80
Mn (%) ≤2.00 ≤2.00
Cr (%) 16.0–18.0 17.0–19.0
Ni (%) 10.0–14.0 9.0–11.0
Mo (%) 2.0–3.0 Not specified
S (%) Not specified ≤0.020
P (%) Not specified ≤0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4303 SUS316 GOST 5632 08X18H10
Tensile Strength ≥520 MPa ≥520 MPa
Yield Strength ≥205 MPa ≥205 MPa
Elongation ≥40% ≥40%
Hardness ≤187 HB Not specified
Typical Applications
JIS G4303 SUS316
Marine applications, chemical processing, pharmaceutical equipment
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can JIS G4303 SUS316 Be Substituted With GOST 5632 08X18H10?
JIS G4303 SUS316 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4303 SUS316
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2800–3300 mm (110.24–129.92 in)
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
JIS G4303 SUS316
3 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4303 SUS316 and GOST 5632 08X18H10?
JIS G4303 SUS316 specifies Mo which is not specified for GOST 5632 08X18H10. GOST 5632 08X18H10 specifies S, P which are not specified for JIS G4303 SUS316.
Can JIS G4303 SUS316 be substituted with GOST 5632 08X18H10?
JIS G4303 SUS316 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.