JIS G4303 SUS410 vs EN 10088-1 X3CrAlTi18-2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

JIS G4303 SUS410 (JIS G4303:2021) and EN 10088-1 X3CrAlTi18-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. JIS G4303 SUS410 is defined under Japanese Industrial Standards (JIS), originating from Japan, while EN 10088-1 X3CrAlTi18-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, JIS G4303 SUS410 vs EN 10088-1 X3CrAlTi18-2 is a 74.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With JIS G4303 SUS410:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 12Kh13 EN 10088-1 1.4301 EN 10088-1 1.4401 GOST 5632 08X18H10 EN 10088-1 1.4845 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
74.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property JIS G4303 SUS410 EN 10088-1 X3CrAlTi18-2
Standard JIS G4303:2021 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) ≤0.15 <=0.04
Si (%) ≤1.00 <=1.00
Mn (%) ≤1.00 <=1.00
Cr (%) 11.5–13.5 17.0-18.0
Ni (%) ≤0.60 Not specified
P (%) ≤0.040 <=0.040
S (%) ≤0.030 <=0.015
Al (%) Not specified 1.70-2.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4303 SUS410 EN 10088-1 X3CrAlTi18-2
Tensile Strength ≥480 MPa (annealed) Not specified
Hardness HRC 36–45 (hardened) Not specified
Elongation ≥20% Not specified
Typical Applications
JIS G4303 SUS410
Cutlery, surgical instruments, turbine blades, fasteners
EN 10088-1 X3CrAlTi18-2
Not documented
Key Differences
Can JIS G4303 SUS410 Be Substituted With EN 10088-1 X3CrAlTi18-2?
JIS G4303 SUS410 and EN 10088-1 X3CrAlTi18-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4303 SUS410
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3100 mm (98.43–122.05 in)
EN 10088-1 X3CrAlTi18-2
No active listings currently.
On M-EX Right Now
JIS G4303 SUS410
3 active listings and RFQs →
EN 10088-1 X3CrAlTi18-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4303 SUS410 and EN 10088-1 X3CrAlTi18-2?
JIS G4303 SUS410 specifies Ni which is not specified for EN 10088-1 X3CrAlTi18-2. EN 10088-1 X3CrAlTi18-2 specifies Al which is not specified for JIS G4303 SUS410.
Can JIS G4303 SUS410 be substituted with EN 10088-1 X3CrAlTi18-2?
JIS G4303 SUS410 and EN 10088-1 X3CrAlTi18-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.