JIS G4303 SUS410 vs IS 1570 (Part 7) 12Cr12Ni2Mo

Minimal Match — 32.8% match based on chemical composition and mechanical property overlap.

JIS G4303 SUS410 (JIS G4303:2021) and IS 1570 (Part 7) 12Cr12Ni2Mo (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. JIS G4303 SUS410 is typically used for cutlery, surgical instruments, turbine blades, fasteners, while IS 1570 (Part 7) 12Cr12Ni2Mo is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. JIS G4303 SUS410 is defined under Japanese Industrial Standards (JIS), originating from Japan, while IS 1570 (Part 7) 12Cr12Ni2Mo is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, JIS G4303 SUS410 vs IS 1570 (Part 7) 12Cr12Ni2Mo is a 49.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32.8%.

Frequently Compared With JIS G4303 SUS410:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 GOST 5632 12Kh13 EN 10088-1 1.4401 GOST 5632 08X18H10 EN 10088-1 1.4845 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
49.1%
MECHANICAL MATCH
0%
OVERALL
32.8%
Specifications
Property JIS G4303 SUS410 IS 1570 (Part 7) 12Cr12Ni2Mo
Standard JIS G4303:2021 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) ≤0.15 0.08-0.16
Si (%) ≤1.00 <=0.35
Mn (%) ≤1.00 0.50-0.90
Cr (%) 11.5–13.5 11.0-12.5
Ni (%) ≤0.60 2.0-3.0
P (%) ≤0.040 <=0.040
S (%) ≤0.030 <=0.030
Mo (%) Not specified 1.5-2.00
V (%) Not specified 0.25-0.40
N (%) Not specified 0.02-0.04
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property JIS G4303 SUS410 IS 1570 (Part 7) 12Cr12Ni2Mo
Tensile Strength ≥480 MPa (annealed) 930-1130 MPa
Hardness HRC 36–45 (hardened) Not specified
Elongation ≥20% >=14%
Yield Strength Not specified >=785 MPa (0.2 % proof stress)
Condition Not specified Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
JIS G4303 SUS410
Cutlery, surgical instruments, turbine blades, fasteners
IS 1570 (Part 7) 12Cr12Ni2Mo
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can JIS G4303 SUS410 Be Substituted With IS 1570 (Part 7) 12Cr12Ni2Mo?
JIS G4303 SUS410 and IS 1570 (Part 7) 12Cr12Ni2Mo share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
JIS G4303 SUS410
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3100 mm (98.43–122.05 in)
IS 1570 (Part 7) 12Cr12Ni2Mo
No active listings currently.
On M-EX Right Now
JIS G4303 SUS410
3 active listings and RFQs →
IS 1570 (Part 7) 12Cr12Ni2Mo
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between JIS G4303 SUS410 and IS 1570 (Part 7) 12Cr12Ni2Mo?
IS 1570 (Part 7) 12Cr12Ni2Mo specifies Mo, V, N which are not specified for JIS G4303 SUS410.
Can JIS G4303 SUS410 be substituted with IS 1570 (Part 7) 12Cr12Ni2Mo?
JIS G4303 SUS410 and IS 1570 (Part 7) 12Cr12Ni2Mo share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.