ASTM A276/A276M S82441 vs EN 10088-1 1.4401

Minimal Match — 36.3% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S82441 (ASTM A276/A276M:2017) and EN 10088-1 1.4401 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S82441 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4401 is commonly used for marine, chemical processing, pharmaceutical equipment. ASTM A276/A276M S82441 is defined under ASTM International, originating from United States, while EN 10088-1 1.4401 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S82441 vs EN 10088-1 1.4401 is a 54.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 36.3%.

Frequently Compared With ASTM A276/A276M S82441:
EN 10088-1 1.4845 ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4301 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
54.4%
MECHANICAL MATCH
0%
OVERALL
36.3%
Specifications
Property ASTM A276/A276M S82441 EN 10088-1 1.4401
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.07
Mn (%) 2.5-4.0 ≤2.00
P (%) <=0.035 Not specified
S (%) <=0.005 Not specified
Cr (%) 23.0-25.0 16.5–18.5
Ni (%) 3.0-4.5 10.5–13.5
Mo (%) 1.00-2.00 2.0–2.5
N (%) 0.20-0.30 Not specified
Cu (%) 0.10-0.80 Not specified
Si (%) Not specified ≤1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S82441 EN 10088-1 1.4401
Tensile Strength >=740 MPa ≥520 MPa
Yield Strength >=540 MPa ≥210 MPa
Elongation >=25% ≥40%
Hardness <=290 HB ≤215 HB
Condition Condition A (Annealed), hot-finished or cold-finished, under 7/16 [11 mm] sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S82441
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4401
Marine, chemical processing, pharmaceutical equipment
Key Differences
Can ASTM A276/A276M S82441 Be Substituted With EN 10088-1 1.4401?
ASTM A276/A276M S82441 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S82441
No active listings currently.
EN 10088-1 1.4401
Sheet → (4 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3400 mm (98.43–133.86 in)
On M-EX Right Now
ASTM A276/A276M S82441
0 active listings and RFQs →
EN 10088-1 1.4401
4 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S82441 and EN 10088-1 1.4401?
ASTM A276/A276M S82441 specifies P, S, N, Cu which are not specified for EN 10088-1 1.4401. EN 10088-1 1.4401 specifies Si which is not specified for ASTM A276/A276M S82441.
Can ASTM A276/A276M S82441 be substituted with EN 10088-1 1.4401?
ASTM A276/A276M S82441 and EN 10088-1 1.4401 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.