ASTM A276/A276M S82441 vs GOST 5632 06Kh23N28

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S82441 (ASTM A276/A276M:2017) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S82441 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications. ASTM A276/A276M S82441 is defined under ASTM International (United States).

As per chemical composition, ASTM A276/A276M S82441 vs GOST 5632 06Kh23N28 is a 60% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S82441:
EN 10088-1 1.4845 ASTM A959 .- EN 10088-1 1.4301 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
60%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property ASTM A276/A276M S82441 GOST 5632 06Kh23N28
Standard ASTM A276/A276M:2017 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.06
Mn (%) 2.5-4.0 ≤2.00
P (%) <=0.035 Not specified
S (%) <=0.005 Not specified
Cr (%) 23.0-25.0 22.0–25.0
Ni (%) 3.0-4.5 26.0–29.0
Mo (%) 1.00-2.00 Not specified
N (%) 0.20-0.30 Not specified
Cu (%) 0.10-0.80 Not specified
Si (%) Not specified ≤0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S82441 GOST 5632 06Kh23N28
Tensile Strength >=740 MPa ≥510 MPa
Yield Strength >=540 MPa ≥196 MPa
Elongation >=25% ≥35%
Hardness <=290 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, under 7/16 [11 mm] sizes (first row printed) Not specified
Max Service Temp Not specified 1050°C
Typical Applications
ASTM A276/A276M S82441
Stainless steel bars and shapes (hot-finished or cold-finished)
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can ASTM A276/A276M S82441 Be Substituted With GOST 5632 06Kh23N28?
ASTM A276/A276M S82441 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S82441
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
ASTM A276/A276M S82441
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S82441 and GOST 5632 06Kh23N28?
ASTM A276/A276M S82441 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28. GOST 5632 06Kh23N28 specifies Si which is not specified for ASTM A276/A276M S82441.
Can ASTM A276/A276M S82441 be substituted with GOST 5632 06Kh23N28?
ASTM A276/A276M S82441 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.