ASTM A276/A276M S82441 vs GB/T 3280 06Cr19Ni10

Minimal Match — 31.8% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S82441 (ASTM A276/A276M:2017) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S82441 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. ASTM A276/A276M S82441 is defined under ASTM International, originating from United States, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, ASTM A276/A276M S82441 vs GB/T 3280 06Cr19Ni10 is a 47.7% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 31.8%.

Frequently Compared With ASTM A276/A276M S82441:
EN 10088-1 1.4845 ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
47.7%
MECHANICAL MATCH
0%
OVERALL
31.8%
Specifications
Property ASTM A276/A276M S82441 GB/T 3280 06Cr19Ni10
Standard ASTM A276/A276M:2017 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08 max
Mn (%) 2.5-4.0 2.00 max
P (%) <=0.035 0.045 max
S (%) <=0.005 0.030 max
Cr (%) 23.0-25.0 18.00-20.00
Ni (%) 3.0-4.5 8.00-11.00
Mo (%) 1.00-2.00 Not specified
N (%) 0.20-0.30 Not specified
Cu (%) 0.10-0.80 Not specified
Si (%) Not specified 1.00 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S82441 GB/T 3280 06Cr19Ni10
Tensile Strength >=740 MPa 520-720 MPa
Yield Strength >=540 MPa 205-310 MPa
Elongation >=25% 40-60%
Hardness <=290 HB 187 HB max
Condition Condition A (Annealed), hot-finished or cold-finished, under 7/16 [11 mm] sizes (first row printed) Not specified
Typical Applications
ASTM A276/A276M S82441
Stainless steel bars and shapes (hot-finished or cold-finished)
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can ASTM A276/A276M S82441 Be Substituted With GB/T 3280 06Cr19Ni10?
ASTM A276/A276M S82441 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S82441
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
ASTM A276/A276M S82441
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S82441 and GB/T 3280 06Cr19Ni10?
ASTM A276/A276M S82441 specifies Mo, N, Cu which are not specified for GB/T 3280 06Cr19Ni10. GB/T 3280 06Cr19Ni10 specifies Si which is not specified for ASTM A276/A276M S82441.
Can ASTM A276/A276M S82441 be substituted with GB/T 3280 06Cr19Ni10?
ASTM A276/A276M S82441 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.