ASTM A276/A276M S82441 vs EN 10088-1 1.4845

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

ASTM A276/A276M S82441 (ASTM A276/A276M:2017) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. ASTM A276/A276M S82441 is typically used for stainless steel bars and shapes (hot-finished or cold-finished), while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components. ASTM A276/A276M S82441 is defined under ASTM International, originating from United States, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.

As per chemical composition, ASTM A276/A276M S82441 vs EN 10088-1 1.4845 is a 57.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With ASTM A276/A276M S82441:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
57.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property ASTM A276/A276M S82441 EN 10088-1 1.4845
Standard ASTM A276/A276M:2017 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.10
Mn (%) 2.5-4.0 ≤2.00
P (%) <=0.035 Not specified
S (%) <=0.005 Not specified
Cr (%) 23.0-25.0 24.0–26.0
Ni (%) 3.0-4.5 19.0–22.0
Mo (%) 1.00-2.00 Not specified
N (%) 0.20-0.30 Not specified
Cu (%) 0.10-0.80 Not specified
Si (%) Not specified ≤1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property ASTM A276/A276M S82441 EN 10088-1 1.4845
Tensile Strength >=740 MPa ≥515 MPa
Yield Strength >=540 MPa ≥205 MPa
Elongation >=25% ≥40%
Hardness <=290 HB Not specified
Condition Condition A (Annealed), hot-finished or cold-finished, under 7/16 [11 mm] sizes (first row printed) Not specified
Max Service Temp Not specified 1100°C continuous
Typical Applications
ASTM A276/A276M S82441
Stainless steel bars and shapes (hot-finished or cold-finished)
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
Can ASTM A276/A276M S82441 Be Substituted With EN 10088-1 1.4845?
ASTM A276/A276M S82441 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
ASTM A276/A276M S82441
No active listings currently.
EN 10088-1 1.4845
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3200 mm (106.3–125.98 in)
On M-EX Right Now
ASTM A276/A276M S82441
0 active listings and RFQs →
EN 10088-1 1.4845
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between ASTM A276/A276M S82441 and EN 10088-1 1.4845?
ASTM A276/A276M S82441 specifies P, S, Mo, N which are not specified for EN 10088-1 1.4845. EN 10088-1 1.4845 specifies Si which is not specified for ASTM A276/A276M S82441.
Can ASTM A276/A276M S82441 be substituted with EN 10088-1 1.4845?
ASTM A276/A276M S82441 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.