EN 10025-2 E360 vs DIN 1654-2 C8C

Related Material — 61% match based on chemical composition and mechanical property overlap.

EN 10025-2 E360 (EN 10025-2:2019) and DIN 1654-2 C8C (DIN 1654-2:1989-10) are both steel grades. EN 10025-2 E360 is classified under Structural Steel, while DIN 1654-2 C8C is classified under Carbon Steel — a different category, which is worth noting alongside the chemistry match below. EN 10025-2 E360 is typically used for hot rolled products of structural steels, while DIN 1654-2 C8C is commonly used for wire drawing, cold heading, nails. EN 10025-2 E360 is defined under European Standard (EN), originating from Europe, while DIN 1654-2 C8C is defined under Deutsches Institut fur Normung (DIN), originating from Germany.

As per chemical composition, EN 10025-2 E360 vs DIN 1654-2 C8C is a 91.5% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 61%.

Frequently Compared With EN 10025-2 E360:
GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 ASTM A283C
Other Structural Steel Grades to Compare With EN 10025-2 E360:
CSA G40.21 400A
Match Breakdown
CHEMISTRY MATCH
91.5%
MECHANICAL MATCH
0%
OVERALL
61%
Specifications
Property EN 10025-2 E360 DIN 1654-2 C8C
Standard EN 10025-2:2019 DIN 1654-2:1989-10
Category Structural Steel Carbon Steel
P (%) <=0.045 ≤0.040
S (%) <=0.045 ≤0.040
N (%) <=0.012 Not specified
C (%) Not specified ≤0.10
Mn (%) Not specified 0.25–0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 E360 DIN 1654-2 C8C
Tensile Strength 670-830 MPa 300–420 MPa
Yield Strength >=360 MPa Not specified
Elongation >=11% ≥30%
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Typical Applications
EN 10025-2 E360
Hot rolled products of structural steels
DIN 1654-2 C8C
Wire drawing, cold heading, nails
Key Differences
Can EN 10025-2 E360 Be Substituted With DIN 1654-2 C8C?
EN 10025-2 E360 and DIN 1654-2 C8C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-2 E360
No active listings currently.
DIN 1654-2 C8C
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5300–6100 mm (208.66–240.16 in)
On M-EX Right Now
EN 10025-2 E360
0 active listings and RFQs →
DIN 1654-2 C8C
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 E360 and DIN 1654-2 C8C?
Different category: EN 10025-2 E360 is Structural Steel, DIN 1654-2 C8C is Carbon Steel. EN 10025-2 E360 specifies N which is not specified for DIN 1654-2 C8C. DIN 1654-2 C8C specifies C, Mn which are not specified for EN 10025-2 E360.
Can EN 10025-2 E360 be substituted with DIN 1654-2 C8C?
EN 10025-2 E360 and DIN 1654-2 C8C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.