Minimal Match — 32.7% match
based on chemical composition and mechanical property overlap.
EN 10088-1 1.4301 (EN 10088-1:2014) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 1.4301 is typically used for food equipment, chemical vessels, architectural, kitchenware, while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-1 1.4301 vs IS 1570 (Part 7) 12Cr12MoVH is a 49.1% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 32.7%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 1.4301
IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength
≥520 MPa
770-930 MPa
Yield Strength
≥210 MPa
>=585 MPa (0.2 % proof stress)
Elongation
≥45%
>=15%
Hardness
≤215 HB
Not specified
Condition
Not specified
Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
IS 1570 (Part 7) 12Cr12MoVH specifies Mo, V which are not specified for EN 10088-1 1.4301.
Can EN 10088-1 1.4301 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-1 1.4301 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 1.4301 and IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 7) 12Cr12MoVH specifies Mo, V which are not specified for EN 10088-1 1.4301.
Can EN 10088-1 1.4301 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-1 1.4301 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.