Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-1 1.4845 (EN 10088-1:2014) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 1.4845 is typically used for furnace parts, heat exchangers, kiln components, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners..
EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.
As per chemical composition, EN 10088-1 1.4845 vs GB/T 3280 06Cr19Ni10 is a 68.1% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 1.4845
GB/T 3280 06Cr19Ni10
Tensile Strength
≥515 MPa
520-720 MPa
Yield Strength
≥205 MPa
205-310 MPa
Elongation
≥40%
40-60%
Max Service Temp
1100°C continuous
Not specified
Hardness
Not specified
187 HB max
Typical Applications
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
GB/T 3280 06Cr19Ni10 specifies P, S which are not specified for EN 10088-1 1.4845.
Can EN 10088-1 1.4845 Be Substituted With GB/T 3280 06Cr19Ni10?
EN 10088-1 1.4845 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 1.4845 and GB/T 3280 06Cr19Ni10?
GB/T 3280 06Cr19Ni10 specifies P, S which are not specified for EN 10088-1 1.4845.
Can EN 10088-1 1.4845 be substituted with GB/T 3280 06Cr19Ni10?
EN 10088-1 1.4845 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.