Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-1 1.4845 (EN 10088-1:2014) and GOST 5632 12Kh13 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-1 1.4845 is typically used for furnace parts, heat exchangers, kiln components, while GOST 5632 12Kh13 is commonly used for turbine blades, pump shafts, fasteners, cutlery.
EN 10088-1 1.4845 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-1 1.4845 vs GOST 5632 12Kh13 is a 75% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-1 1.4845
GOST 5632 12Kh13
Tensile Strength
≥515 MPa
≥540 MPa (annealed)
Yield Strength
≥205 MPa
Not specified
Elongation
≥40%
Not specified
Max Service Temp
1100°C continuous
Not specified
Hardness HRC
Not specified
36–45 (hardened)
Typical Applications
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
Can EN 10088-1 1.4845 Be Substituted With GOST 5632 12Kh13?
EN 10088-1 1.4845 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-1 1.4845 and GOST 5632 12Kh13?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-1 1.4845 be substituted with GOST 5632 12Kh13?
EN 10088-1 1.4845 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.