EN 10088-2 X2CrMnNiTi12 vs ASTM A959 S41003

Close Alternative — 80.7% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrMnNiTi12 (EN 10088-2:2014) and ASTM A959 S41003 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrMnNiTi12 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A959 S41003 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-2 X2CrMnNiTi12 is defined under European Standard (EN), originating from Europe, while ASTM A959 S41003 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-2 X2CrMnNiTi12 vs ASTM A959 S41003 is a 80.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 80.7%.

Frequently Compared With EN 10088-2 X2CrMnNiTi12:
GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
80.7%
MECHANICAL MATCH
No shared data
OVERALL
80.7%
Specifications
Property EN 10088-2 X2CrMnNiTi12 ASTM A959 S41003
Standard EN 10088-2:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 1.00-2.50 <=1.50
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.030
Cr (%) 11.0-13.0 10.5-12.5
Ni (%) 0.30-1.00 <=1.50
N (%) <=0.025 <=0.030
Ti (%) <=0.35 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrMnNiTi12 ASTM A959 S41003
Tensile Strength 500-650 MPa Not specified
Condition Annealed (+A), hot rolled strip, up to 10 mm thick; Yield Strength is Rp0.2 (transverse; longitudinal not given); Elongation is A80 (under 3 mm) or A (3 mm and over) Not specified
Elongation >=20% Not specified
Yield Strength >=375 MPa Not specified
Typical Applications
EN 10088-2 X2CrMnNiTi12
General purposes, hot or cold rolled sheet/plate and strip
ASTM A959 S41003
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can EN 10088-2 X2CrMnNiTi12 Be Substituted With ASTM A959 S41003?
EN 10088-2 X2CrMnNiTi12 and ASTM A959 S41003 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-2 X2CrMnNiTi12
0 active listings and RFQs →
ASTM A959 S41003
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrMnNiTi12 and ASTM A959 S41003?
EN 10088-2 X2CrMnNiTi12 specifies Ti which is not specified for ASTM A959 S41003.
Can EN 10088-2 X2CrMnNiTi12 be substituted with ASTM A959 S41003?
EN 10088-2 X2CrMnNiTi12 and ASTM A959 S41003 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.