GOST 5632 06Kh23N28 vs ASTM A959 304L

Related Material — 67.9% match based on chemical composition and mechanical property overlap.

GOST 5632 06Kh23N28 (GOST 5632-2014) and ASTM A959 304L (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. GOST 5632 06Kh23N28 is typically used for furnace components, heat exchangers, high temperature applications, while ASTM A959 304L is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 304L is defined under ASTM International (United States).

As per chemical composition, GOST 5632 06Kh23N28 vs ASTM A959 304L is a 67.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 67.9%.

Frequently Compared With GOST 5632 06Kh23N28:
EN 10088-1 1.4301 EN 10088-1 1.4845 EN 10088-1 1.4006 EN 10088-1 1.4401 ASTM A959 26-3-3 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 29-4 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 16-8-2H ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
67.9%
MECHANICAL MATCH
No shared data
OVERALL
67.9%
Specifications
Property GOST 5632 06Kh23N28 ASTM A959 304L
Standard GOST 5632-2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) ≤0.06 <=0.030
Si (%) ≤0.80 <=1.00
Mn (%) ≤2.00 <=2.00
Cr (%) 22.0–25.0 17.5-19.5
Ni (%) 26.0–29.0 8.0-12.0
P (%) Not specified <=0.045
S (%) Not specified <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 5632 06Kh23N28 ASTM A959 304L
Tensile Strength ≥510 MPa Not specified
Yield Strength ≥196 MPa Not specified
Elongation ≥35% Not specified
Max Service Temp 1050°C Not specified
Typical Applications
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
ASTM A959 304L
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can GOST 5632 06Kh23N28 Be Substituted With ASTM A959 304L?
GOST 5632 06Kh23N28 and ASTM A959 304L share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
ASTM A959 304L
No active listings currently.
On M-EX Right Now
GOST 5632 06Kh23N28
2 active listings and RFQs →
ASTM A959 304L
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 5632 06Kh23N28 and ASTM A959 304L?
ASTM A959 304L specifies P, S which are not specified for GOST 5632 06Kh23N28.
Can GOST 5632 06Kh23N28 be substituted with ASTM A959 304L?
GOST 5632 06Kh23N28 and ASTM A959 304L share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.