GOST 5632 08X18H10 vs ASTM A959 16-8-2H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GOST 5632 08X18H10 (GOST 5632-2014) and ASTM A959 16-8-2H (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. GOST 5632 08X18H10 is typically used for chemical equipment, food processing, general corrosion resistant applications, while ASTM A959 16-8-2H is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). ASTM A959 16-8-2H is defined under ASTM International (United States).

As per chemical composition, GOST 5632 08X18H10 vs ASTM A959 16-8-2H is a 55.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GOST 5632 08X18H10:
EN 10088-1 1.4301 EN 10088-1 1.4845 EN 10088-1 1.4006 EN 10088-1 1.4401 ASTM A959 201 ASTM A959 .- ASTM A959 202 ASTM A959 26-3-3 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 20Cr12MoNiVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
55.8%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property GOST 5632 08X18H10 ASTM A959 16-8-2H
Standard GOST 5632-2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) ≤0.08 0.05-0.10
Si (%) ≤0.80 <=1.00
Mn (%) ≤2.00 <=2.00
Cr (%) 17.0–19.0 14.5-16.5
Ni (%) 9.0–11.0 7.5-9.5
S (%) ≤0.020 <=0.030
P (%) ≤0.035 <=0.045
Mo (%) Not specified 1.50-2.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 5632 08X18H10 ASTM A959 16-8-2H
Tensile Strength ≥520 MPa Not specified
Yield Strength ≥205 MPa Not specified
Elongation ≥40% Not specified
Typical Applications
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
ASTM A959 16-8-2H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can GOST 5632 08X18H10 Be Substituted With ASTM A959 16-8-2H?
GOST 5632 08X18H10 and ASTM A959 16-8-2H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
ASTM A959 16-8-2H
No active listings currently.
On M-EX Right Now
GOST 5632 08X18H10
2 active listings and RFQs →
ASTM A959 16-8-2H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 5632 08X18H10 and ASTM A959 16-8-2H?
ASTM A959 16-8-2H specifies Mo which is not specified for GOST 5632 08X18H10.
Can GOST 5632 08X18H10 be substituted with ASTM A959 16-8-2H?
GOST 5632 08X18H10 and ASTM A959 16-8-2H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.