GOST 5632 08X18H10 vs IS 1570 (Part 7) 12Cr12Ni2Mo

Minimal Match — 30.5% match based on chemical composition and mechanical property overlap.

GOST 5632 08X18H10 (GOST 5632-2014) and IS 1570 (Part 7) 12Cr12Ni2Mo (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. GOST 5632 08X18H10 is typically used for chemical equipment, food processing, general corrosion resistant applications, while IS 1570 (Part 7) 12Cr12Ni2Mo is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 1570 (Part 7) 12Cr12Ni2Mo is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, GOST 5632 08X18H10 vs IS 1570 (Part 7) 12Cr12Ni2Mo is a 45.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 30.5%.

Frequently Compared With GOST 5632 08X18H10:
EN 10088-1 1.4301 EN 10088-1 1.4845 EN 10088-1 1.4006 EN 10088-1 1.4401 ASTM A959 201 ASTM A959 16-8-2H ASTM A959 .- ASTM A959 202 ASTM A959 26-3-3 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 20Cr12MoNiVH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
45.8%
MECHANICAL MATCH
0%
OVERALL
30.5%
Specifications
Property GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12Ni2Mo
Standard GOST 5632-2014 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) ≤0.08 0.08-0.16
Si (%) ≤0.80 <=0.35
Mn (%) ≤2.00 0.50-0.90
Cr (%) 17.0–19.0 11.0-12.5
Ni (%) 9.0–11.0 2.0-3.0
S (%) ≤0.020 <=0.030
P (%) ≤0.035 <=0.040
Mo (%) Not specified 1.5-2.00
V (%) Not specified 0.25-0.40
N (%) Not specified 0.02-0.04
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12Ni2Mo
Tensile Strength ≥520 MPa 930-1130 MPa
Yield Strength ≥205 MPa >=785 MPa (0.2 % proof stress)
Elongation ≥40% >=14%
Condition Not specified Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
IS 1570 (Part 7) 12Cr12Ni2Mo
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can GOST 5632 08X18H10 Be Substituted With IS 1570 (Part 7) 12Cr12Ni2Mo?
GOST 5632 08X18H10 and IS 1570 (Part 7) 12Cr12Ni2Mo share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
IS 1570 (Part 7) 12Cr12Ni2Mo
No active listings currently.
On M-EX Right Now
GOST 5632 08X18H10
2 active listings and RFQs →
IS 1570 (Part 7) 12Cr12Ni2Mo
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 5632 08X18H10 and IS 1570 (Part 7) 12Cr12Ni2Mo?
IS 1570 (Part 7) 12Cr12Ni2Mo specifies Mo, V, N which are not specified for GOST 5632 08X18H10.
Can GOST 5632 08X18H10 be substituted with IS 1570 (Part 7) 12Cr12Ni2Mo?
GOST 5632 08X18H10 and IS 1570 (Part 7) 12Cr12Ni2Mo share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.