GOST 5632 12Kh13 vs EN 10088-1 1.4845

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GOST 5632 12Kh13 (GOST 5632-2014) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. GOST 5632 12Kh13 is typically used for turbine blades, pump shafts, fasteners, cutlery, while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components. EN 10088-1 1.4845 is defined under European Standard (EN) (Europe).

As per chemical composition, GOST 5632 12Kh13 vs EN 10088-1 1.4845 is a 75% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GOST 5632 12Kh13:
EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4301 ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 20Cr12MoNiVH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
75%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property GOST 5632 12Kh13 EN 10088-1 1.4845
Standard GOST 5632-2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.09–0.15 ≤0.10
Si (%) ≤0.80 ≤1.50
Mn (%) ≤0.80 ≤2.00
Cr (%) 12.0–14.0 24.0–26.0
Ni (%) ≤0.60 19.0–22.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 5632 12Kh13 EN 10088-1 1.4845
Tensile Strength ≥540 MPa (annealed) ≥515 MPa
Hardness HRC 36–45 (hardened) Not specified
Yield Strength Not specified ≥205 MPa
Elongation Not specified ≥40%
Max Service Temp Not specified 1100°C continuous
Typical Applications
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Can GOST 5632 12Kh13 Be Substituted With EN 10088-1 1.4845?
GOST 5632 12Kh13 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 5632 12Kh13
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
EN 10088-1 1.4845
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3200 mm (106.3–125.98 in)
On M-EX Right Now
GOST 5632 12Kh13
2 active listings and RFQs →
EN 10088-1 1.4845
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 5632 12Kh13 and EN 10088-1 1.4845?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can GOST 5632 12Kh13 be substituted with EN 10088-1 1.4845?
GOST 5632 12Kh13 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.