GOST 5632 12Kh13 vs IS 1570 (Part 7) 12Cr12MoVH

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GOST 5632 12Kh13 (GOST 5632-2014) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. GOST 5632 12Kh13 is typically used for turbine blades, pump shafts, fasteners, cutlery, while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, GOST 5632 12Kh13 vs IS 1570 (Part 7) 12Cr12MoVH is a 59.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GOST 5632 12Kh13:
EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4301 EN 10088-1 1.4845 ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 20Cr12MoNiVH IS 1570 (Part 7) 12Cr12MoH GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
59.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr12MoVH
Standard GOST 5632-2014 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) 0.09–0.15 0.08-0.16
Si (%) ≤0.80 <=0.60
Mn (%) ≤0.80 0.40-1.00
Cr (%) 12.0–14.0 11.5-13.00
Ni (%) ≤0.60 <=1.0
P (%) Not specified <=0.040
S (%) Not specified <=0.035
Mo (%) Not specified 0.40-0.80
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength ≥540 MPa (annealed) 770-930 MPa
Hardness HRC 36–45 (hardened) Not specified
Yield Strength Not specified >=585 MPa (0.2 % proof stress)
Elongation Not specified >=15%
Condition Not specified Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can GOST 5632 12Kh13 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
GOST 5632 12Kh13 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GOST 5632 12Kh13
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
IS 1570 (Part 7) 12Cr12MoVH
No active listings currently.
On M-EX Right Now
GOST 5632 12Kh13
2 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 5632 12Kh13 and IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 7) 12Cr12MoVH specifies P, S, Mo, V which are not specified for GOST 5632 12Kh13.
Can GOST 5632 12Kh13 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
GOST 5632 12Kh13 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.