IS 11169 (Part 2) X07Cr17 vs ASTM A959 430FSe

Strong Match — 96.8% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X07Cr17 (IS 11169 (Part 2):1989) and ASTM A959 430FSe (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X07Cr17 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while ASTM A959 430FSe is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 430FSe is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X07Cr17 vs ASTM A959 430FSe is a 96.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 96.8%.

Frequently Compared With IS 11169 (Part 2) X07Cr17:
GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 12Kh13 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 08X18H10 EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
96.8%
MECHANICAL MATCH
No shared data
OVERALL
96.8%
Specifications
Property IS 11169 (Part 2) X07Cr17 ASTM A959 430FSe
Standard IS 11169 (Part 2):1989 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.12
Si (%) <=1.0 <=1.00
Mn (%) <=1.0 <=1.25
Cr (%) 16.0-18.0 16.0-18.0
S (%) <=0.030 <=0.06
P (%) <=0.045 <=0.06
Se (%) Not specified >=0.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X07Cr17 ASTM A959 430FSe
Yield Strength (0.2% proof) >=270 MPa Not specified
Tensile Strength 450-600 MPa Not specified
Elongation >=20% Not specified
Condition Annealed reference test piece (Table 6 treatment) Not specified
Typical Applications
IS 11169 (Part 2) X07Cr17
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
ASTM A959 430FSe
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X07Cr17 Be Substituted With ASTM A959 430FSe?
IS 11169 (Part 2) X07Cr17 and ASTM A959 430FSe overlap closely enough on chemistry and mechanical properties that ASTM A959 430FSe is often considered as a substitute for IS 11169 (Part 2) X07Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X07Cr17
0 active listings and RFQs →
ASTM A959 430FSe
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X07Cr17 and ASTM A959 430FSe?
ASTM A959 430FSe specifies Se which is not specified for IS 11169 (Part 2) X07Cr17.
Can IS 11169 (Part 2) X07Cr17 be substituted with ASTM A959 430FSe?
IS 11169 (Part 2) X07Cr17 and ASTM A959 430FSe overlap closely enough on chemistry and mechanical properties that ASTM A959 430FSe is often considered as a substitute for IS 11169 (Part 2) X07Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.