IS 11169 (Part 2) X07Cr17 vs EN 10088-1 1.4006

Minimal Match — 49.1% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X07Cr17 (IS 11169 (Part 2):1989) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X07Cr17 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. IS 11169 (Part 2) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X07Cr17 vs EN 10088-1 1.4006 is a 73.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 49.1%.

Frequently Compared With IS 11169 (Part 2) X07Cr17:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4845 GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
73.6%
MECHANICAL MATCH
0%
OVERALL
49.1%
Specifications
Property IS 11169 (Part 2) X07Cr17 EN 10088-1 1.4006
Standard IS 11169 (Part 2):1989 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.12 0.08–0.15
Si (%) <=1.0 ≤1.00
Mn (%) <=1.0 ≤1.50
Cr (%) 16.0-18.0 11.5–13.5
S (%) <=0.030 Not specified
P (%) <=0.045 Not specified
Ni (%) Not specified ≤0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X07Cr17 EN 10088-1 1.4006
Yield Strength (0.2% proof) >=270 MPa Not specified
Tensile Strength 450-600 MPa ≥540 MPa (annealed)
Elongation >=20% ≥18%
Condition Annealed reference test piece (Table 6 treatment) Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 11169 (Part 2) X07Cr17
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can IS 11169 (Part 2) X07Cr17 Be Substituted With EN 10088-1 1.4006?
IS 11169 (Part 2) X07Cr17 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 11169 (Part 2) X07Cr17
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 11169 (Part 2) X07Cr17
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X07Cr17 and EN 10088-1 1.4006?
IS 11169 (Part 2) X07Cr17 specifies S, P which are not specified for EN 10088-1 1.4006. EN 10088-1 1.4006 specifies Ni which is not specified for IS 11169 (Part 2) X07Cr17.
Can IS 11169 (Part 2) X07Cr17 be substituted with EN 10088-1 1.4006?
IS 11169 (Part 2) X07Cr17 and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.