IS 11169 (Part 2) X07Cr17 vs IS 1570 (Part 7) 12Cr13H

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X07Cr17 (IS 11169 (Part 2):1989) and IS 1570 (Part 7) 12Cr13H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X07Cr17 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while IS 1570 (Part 7) 12Cr13H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 11169 (Part 2) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) 12Cr13H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 2) X07Cr17 vs IS 1570 (Part 7) 12Cr13H is a 76.8% match. As per mechanical properties, the match is 53%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 11169 (Part 2) X07Cr17:
GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 12Kh13 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 08X18H10 EN 10088-1 1.4845 GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
76.8%
MECHANICAL MATCH
53%
OVERALL
35%
Specifications
Property IS 11169 (Part 2) X07Cr17 IS 1570 (Part 7) 12Cr13H
Standard IS 11169 (Part 2):1989 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.12 0.09-0.15
Si (%) <=1.0 <=1.00
Mn (%) <=1.0 <=1.00
Cr (%) 16.0-18.0 11.5-14.00
S (%) <=0.030 <=0.030
P (%) <=0.045 <=0.040
Ni (%) Not specified <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X07Cr17 IS 1570 (Part 7) 12Cr13H
Yield Strength (0.2% proof) >=270 MPa Not specified
Tensile Strength 450-600 MPa 470-670 MPa
Elongation >=20% >=20%
Condition Annealed reference test piece (Table 6 treatment) Bars, forgings, plates, A, thickness up to 160 (first row of Table 3)
Yield Strength Not specified >=265 MPa (0.2 % proof stress)
Typical Applications
IS 11169 (Part 2) X07Cr17
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
IS 1570 (Part 7) 12Cr13H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can IS 11169 (Part 2) X07Cr17 Be Substituted With IS 1570 (Part 7) 12Cr13H?
IS 11169 (Part 2) X07Cr17 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 2) X07Cr17
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr13H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X07Cr17 and IS 1570 (Part 7) 12Cr13H?
IS 1570 (Part 7) 12Cr13H specifies Ni which is not specified for IS 11169 (Part 2) X07Cr17.
Can IS 11169 (Part 2) X07Cr17 be substituted with IS 1570 (Part 7) 12Cr13H?
IS 11169 (Part 2) X07Cr17 and IS 1570 (Part 7) 12Cr13H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.