Minimal Match — 48.7% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X07Cr17 (IS 11169 (Part 2):1989) and GOST 5632 12Kh13 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X07Cr17 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while GOST 5632 12Kh13 is commonly used for turbine blades, pump shafts, fasteners, cutlery.
IS 11169 (Part 2) X07Cr17 is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 11169 (Part 2) X07Cr17 vs GOST 5632 12Kh13 is a 73.1% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 48.7%.
Frequently Compared With IS 11169 (Part 2) X07Cr17:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X07Cr17
GOST 5632 12Kh13
Yield Strength (0.2% proof)
>=270 MPa
Not specified
Tensile Strength
450-600 MPa
≥540 MPa (annealed)
Elongation
>=20%
Not specified
Condition
Annealed reference test piece (Table 6 treatment)
Not specified
Hardness HRC
Not specified
36–45 (hardened)
Typical Applications
IS 11169 (Part 2) X07Cr17
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
Key Differences
IS 11169 (Part 2) X07Cr17 specifies S, P which are not specified for GOST 5632 12Kh13.
GOST 5632 12Kh13 specifies Ni which is not specified for IS 11169 (Part 2) X07Cr17.
Can IS 11169 (Part 2) X07Cr17 Be Substituted With GOST 5632 12Kh13?
IS 11169 (Part 2) X07Cr17 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X07Cr17 and GOST 5632 12Kh13?
IS 11169 (Part 2) X07Cr17 specifies S, P which are not specified for GOST 5632 12Kh13. GOST 5632 12Kh13 specifies Ni which is not specified for IS 11169 (Part 2) X07Cr17.
Can IS 11169 (Part 2) X07Cr17 be substituted with GOST 5632 12Kh13?
IS 11169 (Part 2) X07Cr17 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.