IS 11169 (Part 2) X07Cr17 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X07Cr17 (IS 11169 (Part 2):1989) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X07Cr17 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. IS 11169 (Part 2) X07Cr17 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 11169 (Part 2) X07Cr17 vs GOST 5632 08X18H10 is a 69.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 11169 (Part 2) X07Cr17:
GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 11Cr17Ni13W3TiH EN 10088-1 1.4845 GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
69.3%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 11169 (Part 2) X07Cr17 GOST 5632 08X18H10
Standard IS 11169 (Part 2):1989 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.12 ≤0.08
Si (%) <=1.0 ≤0.80
Mn (%) <=1.0 ≤2.00
Cr (%) 16.0-18.0 17.0–19.0
S (%) <=0.030 ≤0.020
P (%) <=0.045 ≤0.035
Ni (%) Not specified 9.0–11.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X07Cr17 GOST 5632 08X18H10
Yield Strength (0.2% proof) >=270 MPa Not specified
Tensile Strength 450-600 MPa ≥520 MPa
Elongation >=20% ≥40%
Condition Annealed reference test piece (Table 6 treatment) Not specified
Yield Strength Not specified ≥205 MPa
Typical Applications
IS 11169 (Part 2) X07Cr17
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can IS 11169 (Part 2) X07Cr17 Be Substituted With GOST 5632 08X18H10?
IS 11169 (Part 2) X07Cr17 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 11169 (Part 2) X07Cr17
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
IS 11169 (Part 2) X07Cr17
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X07Cr17 and GOST 5632 08X18H10?
GOST 5632 08X18H10 specifies Ni which is not specified for IS 11169 (Part 2) X07Cr17.
Can IS 11169 (Part 2) X07Cr17 be substituted with GOST 5632 08X18H10?
IS 11169 (Part 2) X07Cr17 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.